废旧电视机外壳的热解动力学研究
摘要： 采用热重分析仪对含有八溴联苯醚的电视机外壳(红外分析鉴定为高抗冲聚苯乙烯,high impact styrene, HIPS)进行了真空条件下的热失重实验,研究了不同升温速率下废旧阻燃高抗冲聚苯乙烯的`降解特性、热解动力学,结果表明样品的热化学特征参数随升温速率的提高而明显增大.根据Arrhenius定律和Friedman方法分析研究了对象的热解动力学,所得相关系数均在0.98以上.该研究的结果为废旧高抗冲聚苯乙烯塑料和其他废旧电子电气塑料的资源化、无害化利用提供了可靠的理论参考. Abstract： The pyrolysis of flame retarded TV housings (high impact polystyrene, HIPS) containing octabromodiphenyl ether (O8BDE) was performed under vacuum condition to understand the decomposition behavior. The decomposition temperatures of O8BDE and cracking temperatures of plastics under different heating rates (5 K/min,10 K/min,20 K/min and 40 K/min) were obtained. Analyzing the kinetic parameters with Arrhenius law and Friedman method, the correlating coefficients are all above 0.98. The results obtained in this study provide references for innoxiously recycling HIPS plastic wastes and other wastes of electrical and electronic equipment (WEEE) plastics. 作 者： 陈源 陈烈强 黄华杰 CHEN Yuan CHEN Lie-qiang HUANG Hua-jie 作者单位： 华南理工大学化学与化工学院传热强化与过程节能教育部重点实验室,广东,广州,510640 期 刊： 陕西科技大学学报（自然科学版） ISTIC Journal： JOURNAL OF SHAANXI UNIVERSITY OF SCIENCE AND TECHNOLOGY(NATURAL SCIENCE EDITION) 年，卷(期)： 2008, 26(4) 分类号： X705 TQ013.2 关键词： 高抗冲聚苯乙烯 多溴联苯醚 真空裂解 动力学 Keywords： HIPS polybromodiphenyl ether vacuum pyrolysis kinetic【废旧电视机外壳的热解动力学研究】相关文章：
废旧阻燃电脑外壳的热解动力学12-29
废旧手机塑料外壳的再利用01-07
城市固体废弃物热重分析及热解动力学研究10-06
医疗废物中有机质的热解动力学研究08-03
印刷线路板废弃物的热解与动力学实验研究01-17
污泥的热解特性实验研究07-19
废旧酚醛树脂印刷电路板的热解特征01-04
废轮胎快速热解实验研究11-22
三种海藻的热解特性及动力学分析07-15