固硫渣安定性改良试验研究
摘要： 通过测定雷氏值和无侧限抗压强度来研究沸石灰渣激发剂(HAZ)掺量对安定性的影响.结果表明HAZ不但可以提高改善固硫渣复合水泥的.安定性而且可以很好的提高其强度.最好通过扫描电镜和X射线衍射分析实验试件的水化产物验证了安定性和强度实验得出的结论. Abstract： This paper presents experimental results on the expansion by Le chaterlier tester and the compressive strength. Hydraulic ash-zeolite (HAZ) cementitious material was blended as the chemical activator to study the effects of the activator on the soundness. The results show that HAZ can not only deduce the expansion, but it can also make the prisms compressive strength increased obviously. FT-IR apectroscopic and X-ray diffraction analysis indicated that the main hydrated products of the sample are calcium hydroxide, ettringite, zeolite and calcite, which consistented with the results of the expansion and the strength tests. 作 者： 朱书景 侯浩波 贺杏华 ZHU Shu-jing HOU Hao-bo HE Xing-hua 作者单位： 武汉大学,资源与环境科学学院,湖北,武汉,430079 期 刊： 中山大学学报(自然科学版) ISTICPKU Journal： ACTA SCIENTIARUM NATURALIUM UNIVERSITATIS SUNYATSENI 年，卷(期)： 2007, 46(z1) 分类号： X703 S216.4 关键词： 固硫渣 安定性 水泥熟料 活性氧化钙 胶凝材料 Keywords： cycled fluidized bed ash (CFBA) soundness cement clinker free CaO cementitious material【固硫渣安定性改良试验研究】相关文章：
高温固硫物相硫铝酸钙的生成机理研究01-13
民用型煤固硫剂的研究12-02
无色硫细菌处理含硫废水的试验研究12-28
NEPE固体推进剂化学安定性研究(Ⅱ)-自燃试验研究07-03
杀螟硫磷生产废水的试验研究07-03
昭通市民用型煤固硫脱硫实验研究07-30
芳香醛与硫代巴比妥酸固相缩合反应的研究10-07
高温铜渣气化城市生活垃圾试验研究10-24