Near infrared electrochromic variable optical attenuator based on ruthenium complex and polycrystalline tungsten oxide
A near infrared (NIR) electrochromic attenuator based on a dinuclear ruthenium complex and polycrystalline tungsten oxide was fabricated and characterized. The results show that the use of the NIR-absorbing ruthenium complex as a counter electrode material can improve the device performance. By replacing the visible electrochromic ferrocene with the NIR-absorbing ruthenium complex, the optical attenuation at 1550 nm was enhanced from 19.1 to 30.0 dB and color efficiency also increased from 29.2 to 121.2 cm2/C.
作 者: ZHANG Jidong WU Xianguo YU Hongan YAN Donghang WANG Zhiyuan 作者单位: ZHANG Jidong,WANG Zhiyuan(Changchun Institute of Applied Chemistry, Changchun 130022,China;Department of Chemistry, Carleton University, Ottawa, Canada K1S 5B6)WU Xianguo,YU Hongan(Department of Chemistry, Carleton University, Ottawa, Canada K1S 5B6)
YAN Donghang(Changchun Institute of Applied Chemistry, Changchun 130022,China)
刊 名: 科学通报(英文版) SCI 英文刊名: CHINESE SCIENCE BULLETIN 年,卷(期): 2005 50(23) 分类号: O6 关键词: near infrared electrochromic dinuclear ruthenium complex polycrystalline tungsten oxide optical attenuation