聚氯乙烯燃烧特性及HCl的生成机理
摘要： 采用热重法对聚氯乙烯(PVC)的燃烧过程进行了研究，探讨了聚氯乙烯燃烧特性，并由它们的微分热重曲线计算出它们的.反应动力学参数及对影响反应常数的因素进行了研究。同时，考察了恒速升温和快速升温过程HCl的生成特性。结果表明，PVC的燃烧机理是由三个过程决定的，可用三个一级反应表示。PVC的燃烧过程的第一阶段为脱氯阶段。第二阶段的活化能和指前因子明显低于第一和第三阶段。此阶段为挥发分释放阶段。升温速率的增加导致反应开始温度、最大反应速率以及HCl开始释放温度的升高。 Abstract： The combustion characteristics of polyvinyl chloride (PVC) are investigated by means of thermogravimetry. The combustion activation energy and frequency factor are obtained by Doyle method. It was observed that PVC weight was reduced in three stages with exothermic reaction in its combustion. The first stage was caused by the chlorine removed from PVC. The volatile matter emission from PVC led to the second weight loss stage of PVC. The mechanism of PVC combustion can be expressed by three first-order kinetic equations. The beginning temperature of reaction, the max reaction rate and the temperature of HCl emission were increased with increasing heating rate. 作 者： 作者单位： 期 刊： 燃料化学学报 ISTICEIPKU Journal： JOURNAL OF FUEL CHEMISTRY AND TECHNOLOGY 年，卷(期)： 2000, 28(1) 分类号： X705 关键词： PVC 热重法 燃烧特性 Keywords： PVC thermogravimetry combustion characteristics【聚氯乙烯燃烧特性及HCl的生成机理】相关文章：
聚甲基丙烯酸甲酯的燃烧特性以及CO和CO2的生成机理07-05
硼粒子的点火及燃烧特性07-15
煤自燃生成水的反应机理研究11-03
在磁场作用下水的特性的变化和它的变化机理07-08
AgOx薄膜的光开关特性和机理研究07-19
论企业营销力的生成机理论文10-06
黑液水煤浆的燃烧和污染排放特性研究07-19
甲基环己烷燃烧反应特性的光谱研究07-29
在SBBR中接种硝化菌时SND特性及机理07-16