Scalable synthesis of A2S3 (A=Sb, Bi) submicro/ nanowires using their powders via solvothermal proceeding
Single-crystal A2S3 (A=Sb, Bi) nanowires were successfully prepared via using their powders as precursors by solvothermal proceeding. The reaction temperature and time as well as solvent strongly influence final A2S3 crystalline morphology and size. Experimental results show that Sb2S3 rods prepared in ethylene glycol are thicker than its wires with average diameter of 400 nm prepared in the mixture solvent of ethylene glycol and ethylenediamine at 200 ℃ for 24 h. However, under the same reaction condition, uniform submicrowires of Bi2S3 with average diameter of 150 nm can be obtained. When reaction temperature is decreased to 150 ℃ and reaction time is 40 h, pure Sb2S3 wires cannot be prepared. The possible mechanism is briefly discussed for the transformation of the Sb2S3 powders to their wire-like crystals.
作 者： JI Tianhao LIU Guanrao QI Xingyi YANG Qinglin DENG Yuan GUO Lin 作者单位： Applied Chemistry Department, School of Materials Science and Engineering, Beijing University of Aeronautics and Astronautics, Beijing 100083, China 刊 名： 科学通报（英文版） SCI 英文刊名： CHINESE SCIENCE BULLETIN 年，卷(期)： 2006 51(6) 分类号： O6 关键词： low dimensional structures transformation of crystalline shape chalcogenides semiconducting wires